EMP
Dual layers with mastic and elastomer, water proof insulation tape
EMP is dual layer structure, one layer is made of mastic and the other is Elastomer. Typical application is waterproof, sealing and protecting for wire connectors. Use to repair cable jackets rapidly. And as the cable joints accessories widely used in heat shrink and cold shrink field.
EMP is dual layer structure, one layer is made of mastic and the other is Elastomer. Typical application is waterproof, sealing and protecting for wire connectors. Use to repair cable jackets rapidly. And as the cable joints accessories widely used in heat shrink and cold shrink field.
Features
- Easily installed to provide realiable protection
- Excellent elastic make it easy to cover irregular shape of connectors
- Excellent adhesive and seal for copper, aluminium and power cable jacket materials
- Esay operang and installation with clearly marked
- Excellent weather resistance
- UV-resistance, cross-linked material, never crack
Material
Elastomer, Mastic
Technical data
|
Property |
Test method |
Typical data |
|
Tensile strength |
ASTM D 2671 |
6.0 Mpa Min. |
|
Elongation at break |
ASTM D 2671 |
800% Min. |
|
Dielectric Strength |
IEC 243 |
20kV/mm Min. |
|
Volume resistance |
IEC 93 |
1.0X1015.Ω·cm Min. |
|
Dielectric resistance |
IEC 250 |
2-3 |
|
Adhesive to Steel |
DIN 30672 |
40N/mm Min. |
|
UV resistance |
|
PASS |
|
Cracking testing |
130 °C, 6hours |
No Crack |
|
Operation temp. |
|
-55 to 105 °C |
Dimensions
|
Prolink Part. No |
Width/mm |
Length/m |
Thickness/mm |
Color |
|
EMP-50 |
50 |
3.0 |
1.8 |
Black |
|
Other specification are available upon request. |
||||