PH6(A)
halogen-free, shrinkage ratio 6:1, without/with hot melting adhesive
High shrink-ratio heavy-duty heat shrinkable tubing designed to pass over size connectors and shrink down onto much smaller cable jackets.
The hot meltable adhesive lined tubing provides environmental sealing, excellent insulation and resistance to impact and abrasion, The 6:1 shrink-ratio conforms well to highly variable substrate dimensions and simplyfies cable repair.
Features and Application:
1. Heavy walled, high shrink ratio
2. Stabilized against UV rays
3. Free from paint-wetting inhibiting substances
4. Suitable for complex shapes and dimensions
5. Non-corrosive, Infusible
6. Superior electrical properties
7. Resistant to cold flow(thermally stable)
Available Color: Black
Technical Date:
|
Properties |
Test Method |
Typical Data |
|
Tensile strength |
ASTM D 2671 |
12 MPa minimum |
|
Ultimate elongation |
ASTM D 2671 |
350% minimum |
|
Tensile strength Aging at 150℃for168hrs |
ASTM D 2671 |
12 Mpa minimum |
|
Ultimate elongation after Aging at 150℃for168hrs |
ASTM D 2671 |
300% minimum |
|
Density |
ASTM D 792 |
1.05 g/cm3 |
|
Dielectric strength |
ASTM D 60243 |
20 kV/mm |
|
Volume resistance |
UL 224 |
10 12 Ω.cm |
|
Low temperature flexibility 40℃/4hrs |
ASTM D 2671 |
No cracking of outer jacket |
|
Properties of hotmelt adhesive |
|
|
|
Softening point |
ASTM E28 |
85+/- 5 C |
|
Peel strength (PE) |
Din 30672 |
4N/cm minimum |
|
Water absorption |
ISO 62 |
0.2% maximum |
Dimensions:
|
Prolink Part. No. |
As supplied |
After recovered |
Standard length |
|
|
|
D(Min.) |
d(Max.) |
w(Min.) |
(m/PC)) |
|
PH6(A) 19/3.2 |
19.0 |
3.2 |
3.2 |
1.0-1.22 |
|
PH6(A) 33/6.5 |
33.0 |
5.5 |
3.4 |
1.0-1.22 |
|
PH6(A) 44.4/7.4 |
44.4 |
7.4 |
3.6 |
1.0-1.22 |
|
PH6(A) 50.8/8.3 |
50.8 |
8.3 |
4.7 |
1.0-1.22 |
|
PH6(A) 69.8/11.7 |
69.8 |
11.7 |
4.7 |
1.0-1.22 |
|
PH6(A) 88.9/17.1 |
88.9 |
17.1 |
4.7 |
1.0-1.22 |
|
PH6(A) 119.4/22.9 |
119.4 |
22.9 |
4.7 |
1.0-1.22 |
Specific length is available upon request